Kapex C352
| Category: | PC , Polycarbonate |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Kapex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W4fuWi_Kapex-C352.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kapex C352 PC is a 25 % glass fiber reinforced product for injection moulding in natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (1.60 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 5170 | MPa | ISO 178 |
| Flexural Stress | 128 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 145 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1, 23°C, notch 0.25in: 150 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 300 - 330 | °C | |
| Middle Temperature | 300 - 330 | °C | |
| Front Temperature | 300 - 330 | °C | |
| Nozzle Temperature | 300 - 320 | °C | |
| Mold Temperature | 30.0 - 100 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 30 GFC K1079 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| UBESTA 3020 GX12 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Borealis PP VG602 | Borealis AG | TPO | Borealis PP |
| Paracril® BJLT M30 | INSA | NBR | Paracril® |
| Akulon® S223-HG0 | DSM Engineering Plastics | Nylon 66 | Akulon® |