Generic SBC
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W4RmK9_Generic-SBC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic SBC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 - 1.07 | g/cm³ | ASTM D792 |
| 23°C | 0.886 - 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 1.0 - 15 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 3.4 - 8.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 10.9 - 12.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.60 - 0.68 | % | ASTM D955 |
| 23°C | 0.50 - 2.4 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 47 - 92 | ASTM D2240 | |
| 23°C | 39 - 91 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 1.03 - 33.4 | MPa | ASTM D638 |
| Yield, 23°C | 4.00 - 51.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 14.0 - 64.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.0 - 2.1 | % | ISO 527-2 |
| Fracture, 23°C | 30 - 260 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 2.5 - 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1330 - 1800 | MPa | ASTM D790 |
| 23°C | 1380 - 2460 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 16.5 - 76.5 | MPa | ISO 178 |
| Yield, 23°C | 24.4 - 54.0 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% strain, 23°C | 1.80 - 5.38 | MPa | ISO 37 |
| 200% strain, 23°C | 1.70 - 6.90 | MPa | ISO 37 |
| 300% strain, 23°C | 2.00 - 4.57 | MPa | ASTM D412 |
| 300% strain, 23°C | 1.00 - 8.00 | MPa | ISO 37 |
| Tensile Stress | |||
| Yield, 23°C | 1.70 - 33.0 | MPa | ISO 37 |
| Fracture, 23°C | 3.96 - 20.3 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Fracture, 23°C | 550 - 850 | % | ASTM D412 |
| Fracture, 23°C | 400 - 890 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 19.8 - 104 | kN/m | ASTM D624 |
| 23°C | 18 - 110 | kN/m | ISO 34-1 |
| Compression Set (23°C) | 18 - 36 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.6 - 9.9 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 20 - 110 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C) | 0.602 - 41.6 | J | ASTM D3763 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Upper Temperature Resistance | 150 - 170 | °C | SAE J2236 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 59.6 - 62.7 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 - -59.0 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 62.7 - 90.0 | °C | ASTM D1525 |
| -- | 62.0 - 93.5 | °C | ISO 306 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 37 - 54 | mm/min | ISO 3795 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 88.9 - 93.1 | % | ASTM D1003 |
| Haze | 0.20 - 3.1 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 77.0 | °C | |
| Rear Temperature | 175 - 200 | °C | |
| Middle Temperature | 175 - 200 | °C | |
| Front Temperature | 175 - 200 | °C | |
| Nozzle Temperature | 175 - 195 | °C | |
| Processing (Melt) Temp | 184 - 250 | °C | |
| Mold Temperature | 26.7 - 50.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SBCThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® R-7-121NA | Solvay Specialty Polymers | PPS | Ryton® |
| Torlon® 4000TF | Solvay Specialty Polymers | PAI | Torlon® |
| Xuchuan XCW-45HE-6 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| E-FLEX™ S5040 | Mando Advanced Materials Co., Ltd. | TPE | E-FLEX™ |
| INTEGRAL™ 848 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |