3M™ Dyneon™ Fluoroelastomer FE 5610N

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	W3cNEP_3MDyneonFluoroelastomerFE5610N.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5610N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE5610N has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: injection and transfer moulding Proprietary incorporated cure technology Viscosity modifier Superior flow over regular Dyneon Fluoroelastomer injection moulding grades Improved scorch resistance compared to products marketed as Dyneon Fluoroelastomer with a product class "FC" Excellent mould release Clean running Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5610N is suitable to produce O-rings in an injection moulding process.

Message

3M™ Dyneon™ Fluoroelastomer FE 5610N is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE5610N has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: injection and transfer moulding

Proprietary incorporated cure technology

Viscosity modifier

Superior flow over regular Dyneon Fluoroelastomer injection moulding grades

Improved scorch resistance compared to products marketed as Dyneon Fluoroelastomer with a product class "FC"

Excellent mould release

Clean running

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5610N is suitable to produce O-rings in an injection moulding process.

General Information
Features	Good demoulding performance
Uses	O-rings
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Resin transfer molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	17	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	76		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	5.30	MPa	ASTM D412A
Tensile Strength ²	14.0	MPa	ASTM D412A
Tensile Elongation ³(Break)	220	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	23	%	ASTM D1414
200°C, 70 hr ⁵	15	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
Titalon® 3225AF	Titan Plastics Compounds Co., Ltd.	Nylon 12	Titalon®
Vydyne® 63A	Ascend Performance Materials Operations LLC	Nylon 66	Vydyne®
FLEXAREN® 14006	Innospec Leuna GmbH	EVA	FLEXAREN®
Formolene® L42022B	Formosa Plastics Corporation, U.S.A.	LLDPE	Formolene®
ELASTOSIL® LR 3003/85 A/B	Wacker Chemie AG	Silicone	ELASTOSIL® LR