ASTATAL™ F3054
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTATAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W3ammS_ASTATAL-F3054.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTATAL™ F3054 is a low viscosity (high melt flow) UV stabilized grade in the ASTATAL™ range suited to general purpose injection moulding applications. F3054 offers an excellent balance of processability, rigidity, frictional wear, heat and chemical resistance and UV resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 62.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2620 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 91.2 | MPa | ASTM D790 |
| Shear Strength (2.00 mm) | 54.9 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 54 | J/m | ASTM D256 |
| Tensile Impact Strength (1.60 mm) | 98.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 158 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | |
| Melting Temperature | 165 | °C | DSC |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 165 to 185 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 185 to 205 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 to 2.50 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 881 TFE 10 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Sylvin 8299-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SUPREME GPPS SC203E | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Ecotan B FL CB NAT | Soredi S.p.a. | Nylon 6 | Ecotan B |
| Lucent PP GPP-340 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |