GELOY™ FXW710SK resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W2mgqL_GELOY-FXW710SK-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GELOY FXW710SK is an ASA/SAN injection moulding grade. It is suitable for those applications that require sparkle colour effects. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 7.00 | cm³/10min | |
| 260°C/5.0 kg | 8.00 | cm³/10min | |
| Molding Shrinkage - Flow 1 | 0.40 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.55 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 38.0 | MPa | |
| Break | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 2.5 | % | |
| Break | 4.0 | % | |
| Flexural Modulus 2 | 1900 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 155 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 88.0 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 75.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 86.0 | °C | ISO 306/B50 |
| -- | 91.0 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 5.20 | ||
| 60 Hz | 5.20 | ||
| 1 MHz | 3.21 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.15 | ||
| 60 Hz | 0.15 | ||
| 1 MHz | 0.026 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm, Testing by SABIC | HB | ||
| 3.00 mm, Testing by SABIC | HB | ||
| Glow Wire Flammability Index (3.20 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 19 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 210 to 240 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF13WT6608 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| DIALAC® S310 | UMG ABS, Ltd. | ASA | DIALAC® |
| ALCOM® PA66 910/1.1 CF15 GF20 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Sylvin 4200-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ COLORCOMP™ FR15C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |