Borealis PE LE0563
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W2gU0U_Borealis-PE-LE0563.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LE0563 is a thermoplastic semiconductive compound specifically designed for medium- high and extra-high voltage cable systems requiring improved grounding. It may be used either as a complete jacket or as a thin layer extruded on top of the regular jacket. This compounds permits easy diagnostic testing of the cable to ensure jacket conformity, allowing confirmation of fault-free cable before and after installation. It provides excellent mechanical properties, superior environmental stress crack resistance and good electrical conductivity. Due to the semiconductive properties, it will also provide added protection against lightning. Specifications : LE0563 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure:
Features: LE0563 provides excellent environmental stress crack resistance and good electrical conductivity. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min | |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F0) | > 2000 | hr | ASTM D1693 |
| Moisture Content 1 | 400 | ppm |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Properties - 240 hr (100°C) | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D, 1 sec | 58 | ||
| Shore D, 3 sec | 55 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2/25 |
| Tensile Strain (Break) | 560 | % | ISO 527-2/25 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ISO 3915 | ||
| 23°C | 25 | ohms·cm | |
| 90°C | 50 | ohms·cm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Melt Temperature | 215 to 245 | °C | |
| Die Temperature | 210 | °C |
| Note Message | |
|---|---|
| 1 . | Karl Fischer-titration, 1000 ppm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-75A HF UV | RTP Company | TPV | RTP |
| Shandong Aobang TPU-Polyester 75-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| VeroCyan™ RGD841 | Stratasys | Unspecified | VeroCyan™ |
| NEXT SIGNATURE CAB MG-100 | NEXT Specialty Resins, Inc. | CAB | NEXT SIGNATURE |
| EVALENE® LLDPE LF10182 | JG Summit Petrochemical Corporation | LLDPE | EVALENE® LLDPE |