PRL PC-G10
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W2Xcnz_PRL-PC-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-G10 is a Polycarbonate (PC) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 65.5 | MPa | |
| Break, 3.18 mm | 62.7 | MPa | |
| Flexural Modulus (3.18 mm) | 3790 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 143 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 138 | °C | |
| RTI Elec | UL 746 | ||
| 1.70 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.70 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Str | UL 746 | ||
| 1.70 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.70 mm, ALL | V-2 | ||
| 3.00 mm, ALL | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Processing (Melt) Temp | 302 to 329 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6G MO | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| APEX® 1587 | Teknor Apex Company | PVC, Flexible | APEX® |
| Grupo IDESA HIPS HI-30-L-01 | Grupo IDESA, S.A. de C.V. | SBC | Grupo IDESA HIPS |
| INSULCAST® RTVS 8128 | ITW Polymers Coatings North America | Silicone Rubber, RTV-2 | INSULCAST® RTVS |
| LNP™ STAT-KON™ DE003ER compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |