TAISOX 3210
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W28WTl_TAISOX-3210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 3210 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 3210 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 142 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 157 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 40.2 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 31.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 620 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 840 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 220 | g | ASTM D1922 |
| TD : 38 µm, blown film | 560 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 43 | ASTM D2457 | |
| Clarity | 67.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 K TFE 15 | RTP Company | PARA | RTP |
| Tenogel® ABS A3 G20 PRTA010 AB307 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| Andur 90 AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| EMOPLEN® CP-R 47.70 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| LNP™ LUBRILOY™ D2000I compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |