TES J-50/20/RG
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W0aKQg_TES-J-50-20-RG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Molding Parameters: 4 hours recommended for high tensile strength and smooth surface finish, or for vacuum metalizing. The dry temperature at 16 hours is 180°F. For 2-zone machines, the rear temperature is 600-650°F, and the front temperature is 580-620°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 110 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 5860 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 299 to 316 | °C | |
| Middle Temperature | 310 to 343 | °C | |
| Front Temperature | 316 to 332 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 304 to 329 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 AR 15 TFE 5 | RTP Company | Nylon 66 | RTP |
| Rotec® ABS 1001 TR | ROMIRA GmbH | ABS | Rotec® ABS |
| TEKAPPO™ JF2 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Moplen HP5019 | LyondellBasell Industries | PP Homopolymer | Moplen |
| Hylex® P1025G20FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |