LNP™ STAT-KON™ PFD06 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W09gwS_LNPSTATKONPFD06compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON PFD06 is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PF-30 Product reorder name: PFD06 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.38 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.50 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.91 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11700 | MPa | ASTM D638 |
| Tensile Strength (Break) | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 910 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 206 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 - 6.0 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 FR | RTP Company | Nylon 66 | RTP |
| Cellophane™ 350P00 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Fiberfil® J-60/10 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Petrothene® NA443023 (Blown) | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 2900-75 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |