INSPIRE™ 361
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VzP6K4_INSPIRE-361.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™When 361 high-performance polymers, it is specially developed for film extrusion processing. INSPIRE™361 high-performance polymers have the characteristics of high transparency. INSPIRE 361 application fields of high-performance polymers:
regulatory information INSPIRE™361 high-performance polymers should meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 50 µm, blown film | 810 | MPa | ISO 527-3 |
| 1% secant, TD : 50 µm, blown film | 790 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 47.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 32.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 580 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 500 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature 2 | 129 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 80 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 3.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 模具间隙：1.0 mm 熔体温度：230°C 放大比：2.5:1 |
| Note Message | |
|---|---|
| 1 . | Injection Molding |
| 2 . | Injection Molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ 34-1520 SSM TFPP | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Trademark PE LD2923F | Trademark Plastics Corporation | LDPE | Trademark PE |
| Crastin® FGS600F40 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| GELOY™ EXGY0071 resin | SABIC Innovative Plastics | ASA | GELOY™ |
| ULTEM™ 1285 resin | SABIC Innovative Plastics | PEI | ULTEM™ |