RTV-2 GI-1100
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vz7cLt_RTV-2-GI-1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GI-1100 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-1100 is especially good for molds with deep undercuts and for molds that require flexing for part removal. GI-1100 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can be accelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1100 is extremely useful for those applications where superior elongation and medium durometer are required. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | |
| Shrinkage - Cured | 0.10 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 171 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.936 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 11 | ||
| Resin | Mix Ratio by Volume: 100 Mix Ratio by Weight: 10 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | 65000 to 80000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Blue | ||
| -- 2 | Off White | ||
| Viscosity | |||
| -- 3 | 0.30 to 0.40 | Pa·s | |
| -- 4 | 120 to 140 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 90 to 150 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 5 | 18 to 26 | ||
| Shore A 6 | 21 to 29 | ||
| Tensile Strength | 3.45 to 3.79 | MPa | ASTM D412 |
| Tensile Elongation at Break | 380 to 430 | % | ASTM D412 |
| Tear Strength | 21.9 to 27.1 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Activator |
| 2 . | Base |
| 3 . | Activator |
| 4 . | Base |
| 5 . | 1 Day |
| 6 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3300-90NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Eltex® HD3850UA | INEOS Olefins & Polymers Europe | LMDPE | Eltex® |
| Karina GREEN COLOR CONCENTRATE 40/272-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PETILEN YY B 00552 | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |
| PENTAMID A E15 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |