KumhoSunny ASA XC220
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VyVUgV_KumhoSunny-ASA-XC220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASAXC811 is a type of general ASA resin, with excellent weatherability and high impact . |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 12 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.70 | % | ASTM D955 |
| -- | 0.40 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 47.0 | MPa | ASTM D638 |
| -- | 48.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break | 30 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- 1 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 71.0 | MPa | ASTM D790 |
| -- 2 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 3.20 mm | 220 | J/m | ASTM D256 |
| 23°C 5 | 17 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50, ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 240 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 4J |
| 5 . | 5.5J |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1799 X 117570 A | RTP Company | PPE+PS | RTP |
| SMOKEGUARD™ FP 108 NATURAL | AlphaGary | Fluoropolymer | SMOKEGUARD™ FP |
| Network Polymers PP PPB 25 0110 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| CP PRYME® Polycarbonate PC100RULUV-18M Black | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Gallonprene® GP540-8505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |