XENOY™ X5601WX resin
| Category: | PBT+PC+PET , Polybutylene Terephthalate + PC + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VyU2LE_XENOY-X5601WX-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified PBT+PC+PET, Heat aging improved XENOY |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 1.0 | % | |
| Across Flow : 3.20 mm | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2290 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2/50 |
| Break 3 | 45.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Break 5 | 93 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus 6(50.0 mm Span) | 2210 | MPa | ASTM D790 |
| Flexural Stress | |||
| -- | 82.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 250 | J/m | ASTM D256 |
| 23°C | 820 | J/m | ASTM D256 |
| -30°C 8 | 18 | kJ/m² | ISO 180/1A |
| 23°C 9 | 62 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 55.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 98.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 131 | °C | ASTM D1525 11 |
| -- | 130 | °C | ISO 306/B50 |
| -- | 132 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 7594N-PE-T | TSRC Corporation | SEBS | T-Blend® |
| ADEKA EP-4003S | Adeka Corporation | Epoxy | ADEKA |
| Estane® 58137 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| HiFill® HDPE GF10 CC | Techmer Engineered Solutions | HDPE | HiFill® |
| Huaxia Shenzhou DS608-C | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluoropolymer | Huaxia Shenzhou |