Kingfa JH950-602
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VwnVGv_Kingfa-JH950-602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa JH950-602 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa JH950-602 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 54.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2400 | MPa | ASTM D790 |
| Flexural Strength 4 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 450 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 126 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 28 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 265°CInjection Speed: 60 to 100% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2817-80 White 1475 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Advanced-PP 1100N | Advanced Petrochemical Company | PP Homopolymer | Advanced-PP |
| Desmovit® DP R 3922 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Hostalen GM 5010 T3 S brown | LyondellBasell Industries | HDPE | Hostalen |
| TOTAL Polyethylene Lumicene® M 3421 UV | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |