POLYAXIS® PD 2000
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYAXIS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VwgcuK_POLYAXIS-PD-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaxis PD 2000 is a polypropylene specifically designed for rotational molding. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Rotational Molded) | 25.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Rotational Molded) | 40 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Rotational Molded) | 1290 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (23°C, 3.18 mm, Rotational Molded) | 20 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Rotational Molded) | 120 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8333G HI | BASF Corporation | Nylon 6 | Ultramid® |
| Electroblend® PBT-2800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | Electroblend® |
| INEOS PP H53N-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| MAJORIS DW305 - 8090 | AD majoris | PP, Unspecified | MAJORIS |
| OnForce™ LFT LF6400-5004 X2 NHFR NATURAL | PolyOne Corporation | Nylon 610 | OnForce™ LFT |