VECTRA® S625
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VwaaOO_VECTRA-S625.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low friction and wear resistance. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.80 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 121 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 9500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 152 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 271 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 129 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 227 | °C | ISO 306/B50 |
| Melting Temperature 1 | 350 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 40.0 | °C | |
| Rear Temperature | 345 - 355 | °C | |
| Middle Temperature | 355 - 365 | °C | |
| Front Temperature | 365 - 375 | °C | |
| Nozzle Temperature | 365 - 375 | °C | |
| Processing (Melt) Temp | 365 - 375 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 365 to 375°CZone 4 Temperature: 365 to 375°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-131 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| TEKAFIN™ P730G30 | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| NatureFlex™ NP 140 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Bergamid™ B70 G/GK30 TM-Y UV NC | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Fainplast PVC GK 01359/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |