Order Products : sales@su-jiao.com
CompaDur® 125 GF 20 natural (015)
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | DimeLika Plast GmbH |
| Trademark: | CompaDur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VwaGtk_CompaDur-125-GF-20-natural-015-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT / PET Blend, injection molding grade, 20% glass fibers, very good surface, balanced flow ability and strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.47 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 250 - 275 | °C | |
| Middle Temperature | 250 - 275 | °C | |
| Front Temperature | 250 - 275 | °C | |
| Nozzle Temperature | 265 - 275 | °C | |
| Processing (Melt) Temp | 265 - 275 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 60.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 1.00 - 3.00 | MPa | |
| Back Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 80 | rpm |
| Injection instructions |
|---|
| Melt residence time: 5 to 10 minsNozzle: open |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 4300 G6 HR | BASF Corporation | PBT | Ultradur® |
| NatureFlex™ NVS 90 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Plasmer 2065N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 7833-80 Black 294 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| GELOY™ EXGY0070 resin | SABIC Innovative Plastics | ASA | GELOY™ |