Rilsan® AESN G9 T6L
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VwXefK_Rilsan-AESN-G9-T6L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan® AESN G9 T6L is a Polyamide 12 (Nylon 12) product filled with filler. It can be processed by extrusion, injection molding, or profile extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1070 | 1070 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (235°C/2.16 kg) | 2.00 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption (Saturation) | 1.4 | -- | % | ISO 62 3 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 2360 | 2200 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | 50.0 | 45.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | 5.0 | 7.0 | % | ISO 527-2 6 |
| Nominal strain at break | 33 | > 50 | % | ISO 527-2 7 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 8 | |||
| -30°C | -- | 4.00 | kJ/m² | |
| 23°C | -- | 5.00 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 9 | |||
| -30°C | -- | 111 | kJ/m² | |
| 23°C | -- | 133 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 10 | |||
| 0.45 MPa | 162 | -- | °C | |
| 1.8 MPa | 65.0 | -- | °C | |
| Melting Temperature 11 | 178 | -- | °C | ISO 11357-3 12 |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 13 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface resistivity | -- | 1.0E+14 | ohms | IEC 60093 14 |
| Volume resistivity | -- | 1.0E+12 | ohms·m | IEC 60093 15 |
| Electric strength | 34 | 34 | kV/mm | IEC 60243-1 16 |
| Relative Permittivity | IEC 60250 17 | |||
| 100 Hz | 4.00 | -- | ||
| 1 MHz | 4.00 | -- | ||
| Dissipation Factor | IEC 60250 18 | |||
| 100 Hz | 0.043 | -- | ||
| 1 MHz | 0.023 | -- | ||
| Comparative tracking index | -- | 600 | IEC 60112 19 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | V-2 | -- | ISO 1210 20 | |
| Burning Behav. at thickness h (3.20 mm) | V-2 | -- | ISO 1210 21 | |
| Oxygen index | 22 | -- | % | ISO 4589-2 22 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | 10 °C/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| mPact™ D350 | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| THERMOLAST® K TP8HPN (Series: EX/UV) | KRAIBURG TPE | TPE | THERMOLAST® K |
| XANTAR® MX 1002 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Boda BDF-LG2752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| EVICOM™ RG7/561 | INEOS Compounds | PVC, Rigid | EVICOM™ |