Badamid® C70 M40 MoS2
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VwBkPl_Badamid-C70-M40-MoS2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66/6 M40 MoS2 Mineral filled, lubricated injection moulding grade with high wear resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.48 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 90.0 | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 5.0 | 15 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 6.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 95 | 180 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 5 | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 243 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 100 | -- | °C | |
| some hours | 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 7 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 8 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 9 | 90 | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity 10(1 MHz) | 4.00 | 4.70 | IEC 60250 | |
| Dissipation Factor 11(1 MHz) | 0.016 | 0.16 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 12 | HB | -- | ||
| 1.60 mm 13 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 110x10x4 mm |
| 6 . | 10 K/min, Compound for moulding |
| 7 . | 80x80x1 mm |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 125x13x0.8 mm |
| 13 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® K203 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| VITAMIDE® BR15NT6504 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| COSMOPLENE® AS164 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| Fainplast PVC CTS 01426/2 | Fainplast Compounds S.r.l | PVC Alloy | Fainplast PVC |
| Infino HP-1000H | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |