Mold Max® Stroke

Category:	Silicone , Silicone
Manufacturer:	Smooth-On, Inc
Trademark:	Mold Max®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Vvkyox_Mold-Max-Stroke.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Mold Max® Stroke® is a brushable tin silicone rubber that self-thickens for making fast brush-on molds of almost any model. Properly applied, it will hold a vertical surface and will reproduce the finest detail. Mixed 100A:10B by weight, rubber quickly develops thixotropy and can be applied with a brush or spatula. Working time is 20 minutes, re-coat time is 45 minutes and cure time after the final layer has been applied is 16 hours at room temperature. Mold Max® Stroke® silicone will not stick to most surfaces and will cure with negligible shrinkage to a strong, flexible Shore 30A rubber. 4 thin layers is all that is necessary to make a strong and durable production mold for casting wax, gypsum, concrete or resins (urethane, polyester, etc.). Applications include reproducing sculpture, architectural restoration, candle molds, etc.

Message

Mold Max® Stroke® is a brushable tin silicone rubber that self-thickens for making fast brush-on molds of almost any model. Properly applied, it will hold a vertical surface and will reproduce the finest detail. Mixed 100A:10B by weight, rubber quickly develops thixotropy and can be applied with a brush or spatula. Working time is 20 minutes, re-coat time is 45 minutes and cure time after the final layer has been applied is 16 hours at room temperature.

Mold Max® Stroke® silicone will not stick to most surfaces and will cure with negligible shrinkage to a strong, flexible Shore 30A rubber. 4 thin layers is all that is necessary to make a strong and durable production mold for casting wax, gypsum, concrete or resins (urethane, polyester, etc.). Applications include reproducing sculpture, architectural restoration, candle molds, etc.

General Information
Features	Durable Good Flexibility Good Strength Low Shrinkage
Uses	Modeling Material
Appearance	White
Processing Method	Casting

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.18	g/cm³	ASTM D1475
Specific Volume	0.849	cm³/g	ASTM D1475

Additional Information	Nominal Value	Unit	Test Method
Mixing Ratio	100A:10B by weight

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.20	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	30		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (100% Strain)	0.758	MPa	ASTM D412
Tensile Strength (Break)	3.98	MPa	ASTM D412
Tensile Elongation (Break)	300	%	ASTM D412
Tear Strength ¹	21.9	kN/m	ASTM D624

Thermoset	Nominal Value	Unit	Test Method
Pot Life (23°C)	20	min	ASTM D2471
Demold Time (23°C)	960	min

Note Message
1 .	Die B

Resin Grade	Manufacturer	Category	Trademark
XYRON™ X332V	Asahi Kasei Chemicals Corporation	PPE+PS	XYRON™
Yanshan PE 6600B	SINOPEC Beijing Yanshan Petrochemical	HDPE	Yanshan PE
Cevian®-V 460M	Daicel Polymer Ltd.	ABS	Cevian®-V
DURACON® EB-08	Polyplastics Co., Ltd.	Acetal (POM) Copolymer	DURACON®
Karina CLEAR PVC COMPOUND 80/210-D-AT-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina