Order Products : sales@su-jiao.com
RTP 4000
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VuiqDB_RTP-4000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.36 | % | ASTM D570 |
| Moisture Content | 0.050 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4140 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 29 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648 |
| CLTE - Flow | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.027 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 302 - 329 | °C | |
| Mold Temperature | 93.3 - 149 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ S201A | Asahi Kasei Chemicals Corporation | PPE | XYRON™ |
| AKROMID® B3 S1 natural (3715) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Forprene® 6E1001A75 | SO.F.TER. SPA | TPV | Forprene® |
| HONES® PBT GT20 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |
| LNP™ VERTON™ RVL28 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |