Bio-Flex® F 1137
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VtGNXC_Bio-Flex-F-1137.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Biodegradable and compostable compound for film extrusion, certified according to EN 13432. Used in applications such as waste bags. Bio-Flex® F 1137 / Bio-Flex® Bin Liner (previously Bio-Flex® V 2877) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 to 4.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 to 3.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 310 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 15.5 | MPa | |
| Break | 13.8 | MPa | |
| Tensile Strain (Break) | 430 | % | ISO 527-2 |
| Flexural Modulus | 305 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 11.5 | MPa | ISO 178 |
| Flexural Strain at Break | No Break | ISO 178 | |
| Tensile Strain at Tensile Strength | 420 | % | ISO 527 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Propagation Resistance | ISO 6383-2 | ||
| Elmendorf - MD : 20.0 µm | 100 | kN/m | |
| Elmendorf - TD : 20.0 µm | 290 | kN/m | |
| Film Thickness - Tested | 20 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 20 µm | 515 | MPa | |
| TD : 20 µm | 420 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm | 37.0 | MPa | |
| TD : Yield, 20 µm | 25.0 | MPa | |
| MD : Break, 20 µm | 36.0 | MPa | |
| TD : Break, 20 µm | 24.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Yield, 20 µm | 290 | % | |
| TD : Yield, 20 µm | 460 | % | |
| MD : Break, 20 µm | 290 | % | |
| TD : Break, 20 µm | 460 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | > 155 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ G80A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| ACRYLITE® Sheet Soundstop NT | Evonik Cyro LLC | Acrylic, Unspecified | ACRYLITE® Sheet |
| Diakon® TD642 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| KumhoSunny ABS 770SRS | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Karina WHITE PVC COMPOUND 800-10/177-Y-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |