SCHULAMID® 612 GF 30 H
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VsX4Gu_SCHULAMID-612-GF-30-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced, Polyamide 612 compound, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (245°C/5.0 kg) | 20.0 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 140 | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.3 | 6.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(23°C) | 7500 | -- | MPa | ISO 178 |
| Flexural Stress 2(4.0% strain, 23°C) | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 5.0 | -- | kJ/m² | ISO 179/1eA |
| -30°C | 6.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 50 | -- | kJ/m² | ISO 179/1eU |
| -30°C | 50 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 60 | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 211 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 191 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 214 | -- | °C | ISO 306/A50 |
| -- | 204 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 2.3E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 2.8E+14 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 675 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 675 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 700 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven J-905 | Propilven, S.A. | PP Homopolymer | Propilven |
| Sylvin 9661-85 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ADENE GHFAD | A.D. Compound spa | PP Homopolymer | ADENE |
| Sylvin 9067-80 Grey 9548 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LUVOCOM® 20-0916 VP | LEHVOSS Group | PPA | LUVOCOM® |