Lucel® N145LD
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VsGELz_Lucel-N145LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUCEL N145-LD is a crystalline resin,which shows excellent mechanical thermal and chemical properties in a wide range of temperature for an extended period. In addition it offers good self-lubrication,friction-resistance and abrasion-resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 62.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus 2 | 2660 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 93.8 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.16 | ||
| vs. Itself - Static | 0.12 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 14.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 54 | J/m | ASTM D256 |
| Unnotched Izod Impact | 640 | J/m | ASTM D256 |
| Reverse Notch Izod Impact | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 6.35 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 110 | °C | |
| CLTE - Flow (20 to 80°C) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec | UL 746 | ||
| 0.710 mm | 110 | °C | |
| 1.50 mm | 110 | °C | |
| 3.00 mm | 110 | °C | |
| RTI Imp | UL 746 | ||
| 0.710 mm | 95.0 | °C | |
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 95.0 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 90.0 | °C | |
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 100 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 | |
| Arc Resistance (3.00 mm) | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.710 mm | PLC 0 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.710 mm | PLC 5 | ||
| 1.50 mm | PLC 5 | ||
| 3.00 mm | PLC 4 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm, ALL | HB | ||
| 1.50 mm, ALL | HB | ||
| 3.00 mm, ALL | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 190 to 200 | °C | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Melt Temperature (Aim) | 190 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 68.6 to 118 | MPa | |
| Back Pressure | 3.92 to 7.84 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 15 mm/min |
| 3 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 15 SI 2 | RTP Company | PC | RTP |
| TECOLITE KM-747(J) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| EL-Lene™ D777C | SCG Chemicals Co., Ltd. | LDPE | EL-Lene™ |
| KOPA® KN333G30CRN | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Sumiliteresin® PR-51363F | SBHPP | Phenolic | Sumiliteresin® |