SPECIALTY PARTIALLY AROMATIC POLYAMIDE BLEND
PARTIALLY AROMATIC PA, 65% GLASS FIBER REINFORCED, LOW WARPAGE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.79 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.28 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.050 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.40 | -- | % | ISO 62 |
| Saturated, 23°C | 3.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 25000 | 24000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 270 | 250 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.9 | 2.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 15 | -- | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 3 | 1.0E+11 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | HB | -- | UL 94 | |
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV HW 30 Black | Radici Plastics | Nylon 66 | Radilon® |
| Wellamid® GF13-66 XE-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| ACCUTECH™ HP0339T20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Kingfa JH720 G20 | Kingfa | PC Alloy | Kingfa |
| PALSAFE® R 10 | pal plast GmbH | PC | PALSAFE® |