MAJORIS G310 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vqki5b_MAJORIS-G310---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS G310 - 8229 is a special long glass fibre reinforced polypropylene grade, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties. MAJORIS G310 - 8229 is available both in black (MAJORIS G310 - 8229) and natural (MAJORIS G310). Other colours can be provided on request. APPLICATIONS MAJORIS G310 - 8229 is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS G310 - 8229 make it suitable for:
MAJORIS G310 - 8229 can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus | 6500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 26 | kJ/m² | ISO 179/1eA |
| 23°C | 23 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| CLTE - Flow | ASTM D696 | ||
| -30°C | 5.1E-5 | cm/cm/°C | ASTM D696 |
| 23°C | 4.1E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10%Holding time: as long as practical |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP 5120C | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Laticonther 52/35 CP1/45 | LATI S.p.A. | PP Homopolymer | Laticonther |
| Hylac® GP27 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| Karina BLACK PVC COMPOUND -E 60880-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OPTICITE™ SQZ White | The Dow Chemical Company | Polyolefin, Unspecified | OPTICITE™ |