LNP™ LUBRICOMP™ RFN16 compound
| Category: | Nylon 66 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VqSBoh_LNPLUBRICOMPRFN16compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFN16 is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: wear resistant Also known as: LNP* LUBRICOMP* Compound RFL-4216 Product reorder name: RFN16 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.65 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 168 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8900 | MPa | ISO 178 |
| Flexural Stress | 237 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.40 | ASTM D3702 Modified | |
| With Self-Static | 0.71 | ASTM D3702 Modified | |
| Wear Factor - Washer | 62.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 260 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 249 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NGIM30-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Hyundai EP PA6 LS950 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Sylvin 7833-80 Brown 7467 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dryflex® A1 602502 | ELASTO | SEBS | Dryflex® |
| SABIC® PP PCGH19 | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |