MAGNUM™ 3404
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VqLRKG_MAGNUM-3404.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 3404 is an excellent general purpose extrusion / thermoforming resin with outstanding processability. It combines medium impact with medium-high heat performance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183/B |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.6 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 6.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 2 | ||
| Saturation | 0.50 | % | |
| Equilibrium | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 2150 | MPa | ISO 527-2 |
| -- | 2150 | MPa | ISO 527-2 3 |
| Tensile Stress | |||
| Yield, 3.20 mm, Injection Molded | 43.0 | MPa | ISO 527-2/50 |
| Yield | 43.0 | MPa | ISO 527-2 4 |
| Tensile Strain (Yield, 3.20 mm, Injection Molded) | 2.7 | % | ISO 527-2/50 |
| Nominal strain at break | 40 | % | ISO 527-2 5 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2100 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 8.0 | kJ/m² | ISO 179/2C |
| -30°C, Injection Molded | 13 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 18 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 13 | kJ/m² | ISO 179/2C |
| Charpy impact strength | ISO 179/1eU 6 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 11 | kJ/m² | |
| 23°C, Injection Molded | 19 | kJ/m² | |
| Tensile notched impact strength (23°C) | 68.0 | kJ/m² | ISO 8256/1 7 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa | 104 | °C | ISO 75-2 8 |
| 1.8 MPa, Annealed | 101 | °C | ISO 75-2/A |
| 1.8 MPa | 101 | °C | ISO 75-2 9 |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 10 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 11 |
| Relative Permittivity | IEC 60250 12 | ||
| 100 Hz | 2.80 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | IEC 60250 13 | ||
| 100 Hz | 6.0E-3 | ||
| 1 MHz | 6.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 14(2.00 mm) | 50 | mm/min | ISO 3795 |
| Flame Rating 15 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 16 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 15 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL AC-GP2 | Polymer Resources Ltd. | Acetal (POM) Copolymer | PRL |
| Selar® PA 3426 | DuPont Packaging & Industrial Polymers | Nylon 6I/6T | Selar® PA |
| Hostacom CR 250 F C11274 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Sylvin 4200-88 Clear Green 3210 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RTP 600 UV Z HB | RTP Company | ABS | RTP |