Reny® C-408
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vq5UbR_Reny-C-408.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® C-408 is a Polyarylamide (PARA) material filled with 40% long carbon fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® C-408: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.28 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 34200 | 29900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 287 | 251 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.90 | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 33000 | 31000 | MPa | ISO 178 |
| Flexural Stress | 500 | 450 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 46 | 43 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 238 | 238 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 234 | 226 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS 3001 M | ROMIRA GmbH | ABS | Rotec® ABS |
| Amilan® CM6041XF | Toray Resin Company | Nylon Copolymer | Amilan® |
| Dryflex® A1 600301 | ELASTO | SEBS | Dryflex® |
| EPO-TEK® H77S | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Sarlink® TPE FM-2676B BLK XRD4 (DISCONTINUED) | Teknor Apex Company | TPE | Sarlink® TPE |