Generic PP, Unspecified - Unspecified
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vpz6WT_Generic-PP-Unspecified---Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Unspecified This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.908 to 1.20 | g/cm³ | ASTM D792 |
| 23°C | 0.930 to 1.08 | g/cm³ | ISO 1183 |
| -- | 1140 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 3.6 to 20 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 8.3 to 17 | g/10 min | ISO 1133 |
| Melt volume-flow rate | 5.28 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 to 1.9 | % | ASTM D955 |
| 23°C | 1.1 to 1.4 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.039 to 0.063 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 94 to 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 4060 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield, 23°C | 20.2 to 70.0 | MPa | ASTM D638 |
| Yield | 53.1 | MPa | ISO 527-2 4 |
| 23°C | 19.6 to 29.1 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 7.9 to 9.0 | % | ISO 527-2 |
| Yield | 2.6 | % | ISO 527-2 5 |
| Break, 23°C | 1.0 to 200 | % | ASTM D638 |
| Break, 23°C | 0.80 to 50 | % | ISO 527-2 |
| Nominal strain at break | 3.0 to 50 | % | ISO 527-2 6 |
| Flexural Modulus | |||
| 23°C | 900 to 5240 | MPa | ASTM D790 |
| 23°C | 1100 to 2570 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 30.2 to 36.3 | MPa | ASTM D790 |
| 23°C | 38.5 to 47.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.9 to 9.2 | kJ/m² | ISO 179 |
| Charpy impact strength (23°C) | 34.5 | kJ/m² | ISO 179/1eU 7 |
| Notched Izod Impact (23°C) | 27 to 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 98.1 to 160 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 90.0 to 144 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 47.0 to 75.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 45.0 to 140 | °C | ISO 75-2/A |
| 1.8 MPa | 147 | °C | ISO 75-2 8 |
| Vicat Softening Temperature | |||
| -- | 54.0 to 157 | °C | ISO 306 |
| 50°C/h, B (50N) | 113 | °C | ISO 306 9 |
| CLTE - Flow | 3.4E-5 to 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.1E+2 to 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 650 to 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ S 60G1 V30 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Axiall PVC SP-6235 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| COPYLENE® CH085 | Phillips 66 | PP Homopolymer | COPYLENE® |
| Elastollan® 1170 A | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| ELASTOSIL® LR 3066/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |