Sunny® PA6 HF200
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vpz1is_Sunny-PA6-HF200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP halogen-free flame Polyamide 6 |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.80 to 1.2 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 20 | % | ISO 527-2/5 |
| Flexural Modulus (50.0 mm Span) | 2000 | MPa | ISO 178 |
| Flexural Stress 1 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.6 | kJ/m² | ISO 180/1A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 240 | °C | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan A-9260G/B-6088 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Nylene® 404 | Custom Resins Group | Nylon 6 | Nylene® |
| Karina GRAY PVC COMPOUND 700-DA-18/291-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kareline® PLMS7525 | Plasthill Oy | PLA | Kareline® |
| Plasmer 2055N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |