Ebalta SG 2000 S / Comp. A+B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vpcqg7_Ebalta-SG-2000-S-Comp-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The product group ebalta SG 2000 consists of high-quality, nearly odourless two-component-Polyurethane casting resins without mixed in filler. The filler is stirred in when the components are mixed. There are different resin components available, which are processed with one hardener. The single types differ in potlife and curing time. The fast curing of the materials leads to a short demoulding time. The very thin binding agent effects a high filler content. The addition of different fillers determines the properties and strength. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 74 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1400 to 1600 | MPa | ISO 178 |
| Flexural Stress | 52.0 to 62.0 | MPa | ISO 178 |
| Compressive Stress | 40.0 to 50.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 20 to 28 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 82.0 to 88.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 89 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.08 to 1.12 | g/cm³ | |
| Viscosity (25°C) | 0.040 to 0.050 | Pa·s | |
| Curing Time (20°C) | 0.25 to 0.50 | hr | |
| Pot Life 1(20°C) | 1.5 to 2.5 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 SI 4 | RTP Company | PC | RTP |
| Sicostirolo CR H 3444 | Ravago Group | PS (HIPS) | Sicostirolo |
| MTEGRITY™ HDPE HD360 | M. Holland Company | HDPE | MTEGRITY™ HDPE |
| VESTOSINT® 1301 white | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| Borealis PP HF700SA | Borealis AG | PP Homopolymer | Borealis PP |