Panlite® AM-1300
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vp6GLU_Panlite-AM-1300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC alloy grade (Special modification) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Flow direction : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Fracture | 61.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture | 130 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2150 | MPa | ISO 178 |
| Flexural Stress 2 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 55 | kJ/m² | ISO 179 |
| 23°C | 63 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 123 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer C-19A | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Elastron® D D101.A63.B | Elastron USA, Inc. | SBS | Elastron® D |
| Globalprene® 3411C | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Plexiglas® HFI10G | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Monprene® CP-17270 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |