Capran Medallion® 2500 film Datasheet,Nylon 6,Honeywell-SHANGHAI SUSHENG

Message
CAPRAN MEDALLION® films from Honeywell are biaxially oriented nylon 6 films with excellent strength and barrier properties. They are well suited for a variety of packaging applications.

General Information
Features	High strength Perforation resistance Good cracking resistance Definition, high Good toughness Barrier resin
Uses	Bi-axially Oriented Film Laminate Food packaging
Forms	Films

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D955
Flow : 0.0254mm	1.5 - 2.5	%	ASTM D955
Transverse flow : 0.0254mm	1.0 - 2.0	%	ASTM D955

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.19	ASTM D1894
With self-dynamics	0.50	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
MD : 25 µm	3100	MPa	ASTM D882
TD : 25 µm	2550	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Break, 25 µm	27.6	MPa	ASTM D882
TD : Break, 25 µm	34.5	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 25 µm	1000	%	ASTM D882
TD : Break, 25 µm	80	%	ASTM D882
Oxygen Permeability (25°C, 25 µm)	0.71	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (25 µm, 38°C, 100% RH)	190	g·mm/m²/atm/24 hr	ASTM F1249

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 25.4 µm)	130 - 150		ASTM D2457
Haze (25.4 µm)	2.5 - 3.5	%	ASTM D1003

Additional Information
Yield: 23964 in²/lbTensile Strength @ Break, ASTM D 882, MD: 35000 to 45000 psiTensile Strength @ Break, ASTM D 882, TD: 45000 to 55000 psiElongation @ Break, ASTM 882, MD: 90 to 110%Elongation @ Break, ASTM 882, TD: 70 to 90%Secant Modulus, ASTM D 882, MD: 400000 to 500000 psiSecant Modulus, ASTM D 882, TD: 320000 to 420000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1400 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.40 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.13 to 0.24 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmWater Vapor Transmission ASTM F 1249, 100°F, 100%RH: 11 to 13 g/100 in²/dayOxygen Transmission Rate, ASTM D3985, 77°F, 0%RH: 1.3 to 2.3 cc/100in²/day

Additional Information

Yield: 23964 in²/lbTensile Strength @ Break, ASTM D 882, MD: 35000 to 45000 psiTensile Strength @ Break, ASTM D 882, TD: 45000 to 55000 psiElongation @ Break, ASTM 882, MD: 90 to 110%Elongation @ Break, ASTM 882, TD: 70 to 90%Secant Modulus, ASTM D 882, MD: 400000 to 500000 psiSecant Modulus, ASTM D 882, TD: 320000 to 420000 psiGraves Tear (initial), ASTM D 1004, MD: 1000 to1400 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.40 to 0.60 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.13 to 0.24 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmWater Vapor Transmission ASTM F 1249, 100°F, 100%RH: 11 to 13 g/100 in²/dayOxygen Transmission Rate, ASTM D3985, 77°F, 0%RH: 1.3 to 2.3 cc/100in²/day

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Capran Medallion®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Vp3NUS_Capran-Medallion-2500-film.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Retpol® PDR 9044 UVA	PolyPacific Pty. Ltd.	PP Copolymer	Retpol®
NANTEX® 758Q	Nantex Industry Co., Ltd.	NBR	NANTEX®
NuSil MED-6020	NuSil Technology	Silicone	NuSil
Ebalta AH 110 / SR	Ebalta Kunststoff GmbH	Epoxy	Ebalta
Lucent PP TPP-330	Lucent Polymers, Inc.	PP, Unspecified	Lucent PP