SABIC® HDPE M864EG

Category:	HDPE , High Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® HDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VopYyh_SABICHDPEM864EG.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

SABIC® HDPE M864EG is a high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applications where rigidity, toughness and warp resistance are required. SABIC® HDPE M864EG is available with UV stabilizer as SABIC® HDPE M864SE and M864SG.

Typical applications

Crates & Boxes: SABIC® HDPE M864EG is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items.

Caps & Closures: SABIC HDPE® M864EG is typically used for Juice, Milk and Edible Oil applications.

This product is not intended for and must not be used in any pharmaceutical/medical applications.

General Information
Features	High density Bending resistance Good toughness Narrow molecular weight distribution Medium hardness
Uses	Industrial application Shield Barrel Shell Loading box
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.964	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	8.0	g/10 min	ISO 1133
190°C/5.0 kg	22	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (40°C, 1.00mm, 10% Igepal CO-630, compression molding)	7.00	hr	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	65		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (2.00 mm, Compression Molded)	1450	MPa	ISO 527-2/1BA/50
Tensile Stress			ISO 527-2/1BA/50
Yield, 2.00mm, molded	32.0	MPa	ISO 527-2/1BA/50
Fracture, 2.00mm, molded	15.0	MPa	ISO 527-2/1BA/50
Tensile Strain (Break, 2.00 mm, Compression Molded)	> 200	%	ISO 527-2/1BA/50
Flexural Modulus (2.00 mm, Compression Molded)	1700	MPa	ISO 178
Flexural Stress (2.00 mm, Compression Molded)	32.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, Compression Molded)	4.0	kJ/m²	ISO 180/A

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	94.0	°C	ISO 75-2/B
Vicat Softening Temperature	129	°C	ISO 306/A
Melting Temperature (DSC)	134	°C	ISO 11357-3
Enthalpy Change	226	J/g	ISO 11357-3

Resin Grade	Manufacturer	Category	Trademark
Talcoprene® 320TL NERO	SO.F.TER. SPA	PP Homopolymer	Talcoprene®
Tarnamid® T- 27 MCS	Grupa Azoty S.A.	Nylon 6	Tarnamid®
Zetpol® 2010L	Zeon Corporation	NBR	Zetpol®
BITONER® C9 H-120	Qingdao Bater Chemical Co., Ltd.	TP, Unspecified	BITONER®
Daelim Po1y® 5502-03LD	DAELIM INDUSTRIAL CO., LTD.	HDPE	Daelim Po1y®