NYCOA Polyamide 4025 HV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VoO3dG_NYCOA-Polyamide-4025-HV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 4025 HV is an Ultra-high viscosity resin particularly suitable for thermoforming and blow molding. Its high melt viscosity and strength provide ease of processing for tubes, profiles, and sheet. This material is specifically engineered for applications requiring high stiffness, toughness, and melt strength. NYCOA 4025 is also available in heat stable, UV stable, custom colors, and impact modified grades. Suggested applications include thermoformed storage containers and blow molded articles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 160 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 6300 | MPa | ASTM D790 |
| Flexural Strength 4 | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789.Notched Izod Impact, ASTM D256, 0.25 in: Partial Break |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ L542V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Ultramid® T KR 4355 G10 | BASF Corporation | Nylon 6/6T | Ultramid® |
| Evermore PUR B-666NCW | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Geon™ HTX Ultra LA427Plus | PolyOne Corporation | PVC Alloy | Geon™ HTX Ultra |
| Lytex X-4185 | Quantum Composites Inc. | Epoxy | Lytex |