UBESTA XPA 9063 X1
| Category: | Nylon 12 Elast , Polyamide 12 Elastomer |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VoB3N9_UBESTA-XPA-9063-X1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BESTA XPA 9063 X1 is a thermoplastic polyamide elastomer offering enhanced material properties and good process-ability in injection moulding and extrusion application. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.80 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 2.1 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 37 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 23 | % | ISO 527-2 |
| Fracture | 400 | % | ISO 527-2 |
| Flexural Modulus | 250 | MPa | ISO 178 |
| Flexural Stress | 14.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 96 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 62.0 | °C | ISO 75-2/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| CLTE - Flow | 1.9E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+11 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >400%Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 4 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miflon® 3321 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| Celstran® PA66-GF50-0112P7,5/10 | Celanese Corporation | Nylon 66/6 | Celstran® |
| ELASTOSIL® R 861/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Kuraray K-Polymer KL-118 | Kuraray Co., Ltd. | PVOH | Kuraray K-Polymer |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7502BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |