SABIC® LLDPE 6821W
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vo5kkP_SABIC-LLDPE-6821W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®LLDPE 6821W is a linear low density polyethylene product,. It can be processed by blowing film and is available in Europe. SABIC®The application fields of LLDPE 6821W include packaging, bag/lining, wrapping, film and agriculture. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 30 µm | 210 | MPa | ASTM D882 |
| TD : 30 µm | 230 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 30 µm | 13.0 | MPa | ASTM D882 |
| MD : Break, 30 µm | 55.0 | MPa | ASTM D882 |
| TD : Break, 30 µm | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 600 | % | ASTM D882 |
| TD : Break, 30 µm | 730 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 160 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 300 | g | ASTM D1922 |
| TD : 30 µm | 920 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 30.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| 30µm blown film produced with a blow up ratio of 1:2.5.The film properties are measured on a similar grade without slip agent, antiblock and processing aid (PPA).Puncture Resistance, SABIC Method, 30µm, Blown Film: 70 J/mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 225 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 to 3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL550600-100 (1.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Di-Pak™ E-4701-5 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| LNP™ THERMOCOMP™ RF008 compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |
| TECACOMP® PBT TF natural 3438 | Ensinger GmbH | PBT | TECACOMP® |
| POTICON RM722 | Otsuka Chemical Co., Ltd. | PPS | POTICON |