Catalyst PS/2 Black Datasheet,Polyolefin, Unspecified,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Catalyst PS/2 is a PE based black catalyst masterbatch, which accelerates the crosslinking reaction of the pipe product during its curing process that can take place by exposure of the pipe to water or steam at high temperature. Catalyst PS/2 Black contains a processing aid.

General Information
Features	Antioxidation Good UV resistance Good thermal aging resistance
Uses	Pipe components Piping system Potable water application
Processing Method	Pipeline extrusion molding Extrusion

Physical	Nominal Value	Unit	Test Method
Apparent Density	0.65	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ISO 1133

Additional Information
Above values are typical averagesUse and DosageCatalyst PS/2 Black shall be used together with the silane-crosslinkable POLIDAN® compounds in the ratio of 7 to 93 parts respectively. The two components shall be mixed together before the extrusion or continuously during the process with the use of automatic feeders. Pre-dry is suggested.StorageThe product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within 12 months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled.PackagingCatalyst PS/2 Black is supplied in 25 kg bags placed on pallets.Technical ServiceCatalyst PS/2 Black is part of the Solvay Specialty Polymers catalyst masterbatch range and is used together with the POLIDAN® compounds. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product.

Additional Information

Above values are typical averagesUse and DosageCatalyst PS/2 Black shall be used together with the silane-crosslinkable POLIDAN® compounds in the ratio of 7 to 93 parts respectively. The two components shall be mixed together before the extrusion or continuously during the process with the use of automatic feeders. Pre-dry is suggested.StorageThe product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within 12 months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled.PackagingCatalyst PS/2 Black is supplied in 25 kg bags placed on pallets.Technical ServiceCatalyst PS/2 Black is part of the Solvay Specialty Polymers catalyst masterbatch range and is used together with the POLIDAN® compounds. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product.

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150 - 200	°C
Cylinder Zone 2 Temp.	150 - 200	°C
Cylinder Zone 3 Temp.	150 - 200	°C
Cylinder Zone 4 Temp.	150 - 200	°C
Cylinder Zone 5 Temp.	150 - 200	°C
Head Temperature	200	°C
Extruder Screw L/D Ratio	25:1 ~ 30:1
Extruder Screw Compression Ratio	>2.5:1
Die Temperature	210	°C

Extrusion instructions
Typical extrusion temperatures in combination to POLIDAN® crosslinkable grades

Category:	Polyolefin, Unspecified , Polyolefin
Manufacturer:	Solvay Specialty Polymers
Trademark:	Catalyst
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Vnpf1i_Catalyst-PS-2-Black.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Network Polymers PS CPS 80 1800	Network Polymers, Inc.	PS (GPPS)	Network Polymers PS
AIE PA6 5010F	Asia International Enterprise (Hong Kong) Limited	Nylon 6	AIE PA6
GAZOLE™ 6430CF	Gharda Chemicals Ltd.	PBI	GAZOLE™
K-Guard HFFR 771	Technovinyl Polymers India Ltd.	Polyolefin, Unspecified	K-Guard
Infino VB-5302GR	SAMSUNG SDI CO., LTD.	PBT	Infino