Sinpolene CPP2040
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Teknor Apex Asia Pacific PTE. LTD. |
| Trademark: | Sinpolene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vlv1Ay_Sinpolene-CPP2040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sinpolene CPP2040 is a Polypropylene Copolymer (PP Copolymer) material filled with 40% calcium carbonate. It is available in Asia Pacific for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 to 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 1750 | MPa | ASTM D790 |
| Flexural Strength | 32.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 146 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 30 HS MS 2 | RTP Company | Nylon 66 | RTP |
| Biograde D-2M | Biograde Group of Companies | Biodeg Polymers | Biograde |
| HiFill® PC/PBT IM 6370 GF30 | Techmer Engineered Solutions | PC+PBT | HiFill® |
| INNOBATCH® PPH 3260 | Inno-Comp Ltd. | PP Homopolymer | INNOBATCH® |
| Karina WHITE PVC COMPOUND 802D10/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |