Escorene™ Ultra LD 726.07
| Category: | EVA , Ethylene Vinyl Acetate Copolymer Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Escorene™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VltDoH_Escorene-Ultra-LD-726-07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LD726.07 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. LD726.07 is an excellent sealing material with a very low seal initiation temperature and high clarity. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% | ExxonMobil Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 15 sec | > 90 | ||
| Shore D, 15 sec | 34 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - MD (Break) | 7.45 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | > 800 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 55.0 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC5-12B40 | Spartech Polycom | PP Homopolymer | Spartech |
| Torayca® TLP8148 | Toray Resin Company | PP, Unspecified | Torayca® |
| Eraclene® MS 80 U | Versalis S.p.A. | HDPE | Eraclene® |
| LNP™ THERMOCOMP™ DF0029ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Moplen EP546T | LyondellBasell Industries | PP Impact Copolymer | Moplen |