MAGNUM™ 3404 Smooth
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vkvf0K_MAGNUM-3404-Smooth.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 3404 Smooth is an excellent general purpose extrusion / thermoforming resin with outstanding processability. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. The new MAGNUM 'Smooth Series' resins have an ultra low particulate content, which results in a superb surface finish that will enable our customers to produce parts with excellent aesthetics at a lower total cost. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.7 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 6.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2150 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 3.20 mm, Injection Molded) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 3.20 mm, Injection Molded) | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2100 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 13 | kJ/m² | ISO 179/1eA |
| -30°C, Injection Molded | 8.0 | kJ/m² | ISO 179/2C |
| 23°C, Injection Molded | 18 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 13 | kJ/m² | ISO 179/2C |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 11 | kJ/m² | |
| 23°C, Injection Molded | 19 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(2.00 mm) | 50 | mm/min | ISO 3795 |
| Flame Rating 2 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 RC HS Black | RTP Company | Nylon 66 | RTP |
| Diofan® A 050 | Solvay Specialty Polymers | PVDC | Diofan® |
| Kingfa JH720 G50 | Kingfa | PC Alloy | Kingfa |
| Pearlbond™ 503 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| CYCOLAC™ INP630 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |