Lutene® XL2700BK TR
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vk8IAN_Lutene-XL2700BK-TR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Description: LUTENE® XL2700BK TR was specially designed crosslinkable semi-conductive compound for easy strippable insulation shielding of medium and high voltage power cable. LUTENE® XL2700BK TR provides an excellent stripping property, lower and consistent stripping force over a wide temperature range without tearing, leaving a clean insulation surface. Especially LUTENE® XL2700BK TR has an excellent tree retardant propety. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ASTM D1505 |
| Moisture Content | < 500 | ppm | Karl Fisher |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Tensile Elongation 1 | > 90 | ppm | ASTM D638 |
| Retention of Tensile Strength 2 | > 90 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Creep | ICEA T-28-562 | ||
| Hot | < 100 | % | |
| Set | < 5.0 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content - Metal | < 1000 | % | Internal Method |
| Stripping Force (1.27 cm) 3 | 3500 to 7000 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -50.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D991 | ||
| 23°C | < 1.0E+2 | ohms·cm | |
| 90°C | < 1.0E+3 | ohms·cm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 | °C | |
| Melt Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 121°C, 168 Hr |
| 2 . | 121°C, 168 Hr |
| 3 . | kg/12.7 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PP 40 TALC | RTP Company | PP, Unspecified | RTP |
| Sup-tech P240 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| THORNEL® GPC-10 | Cytec Industries Inc. | Carbon/Epoxy | THORNEL® |
| Viprene™ P75A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| ICORENE® N4506 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | ICORENE® |