Miramid® S3CHW
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Leuna GmbH |
| Trademark: | Miramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ViViyA_Miramid-S3CHW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Miramid® S3CHW is a Polyamide 66 (Nylon 66) material. It is available in Europe for injection molding. Important attributes of Miramid® S3CHW are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1130 | -- | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | |||
| Saturation | 7.5 | -- | % | |
| Equilibrium | 2.5 | -- | % | |
| Viscosity number | 145 | -- | cm³/g | ISO 307, 1157, 1628 3 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 3000 | 1800 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | 80.0 | 60.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | 5.0 | 20 | % | ISO 527-2 6 |
| Nominal strain at break | 10 | > 50 | % | ISO 527-2 7 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 8 | |||
| -30°C | 3.00 | -- | kJ/m² | |
| 23°C | 4.00 | 20.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 9 | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 10 | |||
| 0.45 MPa | 200 | -- | °C | |
| 1.8 MPa | 70.0 | -- | °C | |
| Melting Temperature 11 | 260 | -- | °C | ISO 11357-3 12 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume resistivity | 1.0E+13 | 1.0E+10 | ohms·m | IEC 60093 13 |
| Relative Permittivity (1 MHz) | 3.40 | 5.00 | IEC 60250 14 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 15 | |
| Comparative tracking index | -- | 600 | IEC 60112 16 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 17 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | 10 °C/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 D | RTP Company | Nylon 612 | RTP |
| PRIMATOP PP HOMO 120NA-HF | Amco Polymers | PP Homopolymer | PRIMATOP |
| CarmelStat™ CS 1015 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| FINGERPRINT™ MDPE 7520 NT | The Dow Chemical Company | MDPE | FINGERPRINT™ |
| Sylvin 2984-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |