AZDEL™ C321-B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vgeqvy_AZDEL-C321-B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL® C321-B01 is a glass mat thermoplastic laminate based upon random oriented chopped fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural thin wall applications and where good glass distribution into features such as ribs and bosses is desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4620 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 76.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 4570 | MPa | ISO 178 |
| Flexural Stress | 104 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy to Peak Load | 8.95 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 13.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 151 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 5.1 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Filler Content by Weight (Ashing), Internal Test Method: 32%Specific Gravity, ASTM D792, Laminate: 1.12Specific Gravity, ASTM D792, Molded: 1.14Sheet Thickness, Internal Test Method: 142 milsBasis Weight (Mass per unit area), Internal Test Method: 0.82 lbs/ft²Instrumented Dart Impact Peak Force, ASTM D3763, 4.0 mm: 480 lbPoisson's Ratio, ISO 527: 0.317Notched Izod Impact Strength, ISO 180, 23°C: 560 J/m |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 8536B | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Sindustris PE XL8081TR | Sincerity Australia Pty Ltd. | PE, Unspecified | Sindustris PE |
| Vi-Chem PVC VSR50D-80I-8816 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| EL-Lene™ H1000PC | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Hostacom M4 U02 102943 Blk | LyondellBasell Industries | PP Homopolymer | Hostacom |