Luranyl® HT 220 G6
| Category: | PPE+Nylon 66 , Polyphenylene Ether + Nylon 66 |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Luranyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VgQpmF_Luranyl-HT-220-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PA Blend with 30% glass fibre; impact resistant; very high heat resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 45.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (23°C, 3.20 mm) | 0.20 - 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 140 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 8.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 285 - 310 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Maximum Residence Time: 4 to 10 minInjection Pressure: moderate to high |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 V30 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TAIRILAC AG10AP | Formosa Plastics Corporation | ABS | TAIRILAC |
| Cellidor CP 3406-08 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| ISPLEN® PM284 AV | REPSOL | PP Copolymer | ISPLEN® |
| Lupol® HG3100 | LG Chem Ltd. | PP, Unspecified | Lupol® |