Chemlon® 104-13 G
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VgHq5t_Chemlon-104-13-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 104-13 G is a Polyamide 66 (Nylon 66) material filled with 13% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 104-13 G are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (285°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 7.0 | % | |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Flexural Strength | 134 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | °C | ASTM D648 |
| Melting Temperature | 257 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 11 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| FMVSS Flammability | PASSES | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 257 | °C | |
| Middle Temperature | 257 to 274 | °C | |
| Front Temperature | 263 to 282 | °C | |
| Nozzle Temperature | 263 to 279 | °C | |
| Processing (Melt) Temp | 263 to 279 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 371A4000012 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Vipel® K023-AAA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Flontech® FT-CARR25-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| OTECH TPE OTR3595 - Profile | OTECH Corporation | TPE | OTECH TPE |
| POCAN® C 1202 000000 | LANXESS Asia/Pacific | PC+PBT | POCAN® |