Hytrel® 3078
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vg4d0C_Hytrel-3078.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30 Shore D High Performance Polyester Elastomer with Non-discoloring Stabilizer |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.60 | % | |
| Flow | 0.60 | % | |
| Water Absorption | |||
| 24 hr | 0.50 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 30 | ||
| Shore D, 15 sec | 26 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 24.0 | MPa | |
| 10% Strain | 1.80 | MPa | |
| 50% Strain | 5.00 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 900 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 22.0 | MPa | |
| 1000 hr | 18.0 | MPa | |
| Flexural Modulus | 21.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 77 | kN/m | |
| Flow | 80 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -98.0 | °C | ISO 974 |
| Glass Transition Temperature 1 | -60.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 177 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-4 | cm/cm/°C | |
| Transverse | 2.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 9.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.90 | ||
| 1 MHz | 4.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | ||
| 1 MHz | 0.013 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 19 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 0.940 | g/cm³ | |
| Specific Heat Capacity of Melt | 2150 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.15 | W/m/K |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Evoprene™ GC 5694 | AlphaGary | SEBS | Evoprene™ GC |
| DOMAMID® 6G30 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| INLUBE PPACF10TF10 | Infinity LTL Engineered Compounds | PPA | INLUBE |
| Plaslube® PA6/6 GF40 IM HS L BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| TechnoPet GF 45 2 1 | TechnoCompound GmbH | PET | TechnoPet |