LNP™ THERMOCOMP™ RF0039S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VfxgDN_LNP-THERMOCOMP-RF0039S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1003 FR HS Product reorder name: RF0039S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.49 | g/cm³ | ASTM D792 |
| -- | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.89 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.49 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6070 | MPa | ASTM D638 |
| -- | 6300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 101 | MPa | ASTM D638 |
| Break | 98.4 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5170 | MPa | ASTM D790 |
| -- | 600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 160 | MPa | ASTM D790 |
| -- | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 520 | J/m | ASTM D4812 |
| 23°C 3 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.70 | J | ASTM D3763 |
| -- | 1.71 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 227 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 219 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.70 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3GM35 BK60564 | BASF Corporation | Nylon 6 | Ultramid® |
| Fainplast PVC PH 50/AL | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Generic TPC-ET | Generic | TPC-ET | Generic |
| Keysor PVC KYHH | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| OXPEKK® SP | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |